PENGARUH REDUKSI CANAI TERHADAP SIFAT MEKANIS BAJA KARBON RENDAH DENGAN SAMBUNGAN FLASH BUTT WELDING

  • Sunardi Klaten Jurusan Teknik Mesin, Universitas Sultan Ageng Tirtayasa

Abstract

Steel plate making can be produced by hot and cold rolling method. To obtain the optimal results, the production on the cold rolling mill (CRM) must be carried out continuously. This CRM is equipped with a flash butt welding machine to connect between one plate and anothers. The purpose of this research is to determine the effect of thickness reduction on mechanical properties of steel JIS 3141. The method used in this study is experimental, namely mechanical properties testing at weld area, heat affected zone (HAZ) and base material. The thickness reductions used in this research are 0%, 69,78%, 71,56% and 73,33%. The material characteristics observed were hardness, tensile strength, yield strength, elaongation and corrosion rate. From this study it is known that the thickness reduction 73.33% resulted the best mechanical properties. The values ​​of hardness, tensile strength, yield strength and corrosion rate were 82.26 HRB, 644 N / mm2, 501 N / mm2 and 1.3844 mpy, respectively.

Keywords: Cold rolling, thickness reduction, mecahincal properties, corrosion rate

Downloads

Download data is not yet available.

References

[1] B. B. Singh, K. S. Kumar, V. Madhu, and R. A. Kumar, “Effect of Hot Rolling on Mechanical Properties and Ballistic Performance of High Nitrogen Steel,” in Procedia Engineering, 2017, vol. 173, pp. 926–933.
[2] S. K. Ghosh, D. Mahata, R. Roychaudhuri, and R. Mondal, “Effect of rolling deformation and solution treatment on microstructure and mechanical properties of a cast duplex stainless steel,” Bull. Mater. Sci., vol. 35, no. 5, pp. 839–846, Oct. 2012.
[3] Suyitno, B. Arifvianto, T. D. Widodo, M. Mahardika, P. Dewo, and U. A. Salim, “Effect of cold working and sandblasting on the microhardness, tensile strength and corrosion resistance of AISI 316L stainless steel,” Int. J. Miner. Metall. Mater., vol. 19, no. 12, pp. 1093–1099, Dec. 2012.
[4] Sunardi, R. Lusiani, and A. S. Irawan, “Karakteristik Sifat Mekanis dan Struktur Mikro Material Hasil Proses Forging,” J. Manutech, vol. 4, no. 1, pp. 12–17, 2012.
[5] C. A. I. Zhipeng, N. Masashi, M. A. Ninshu, Q. U. Yuebo, and C. A. O. Bin, “Residual Stresses in Flash Butt Welded Rail †,” vol. 40, no. 1, pp. 79–87, 2011.
[6] D. C. Kim, W. J. So, and M. J. Kang, “Effect of flash butt welding parameters on weld quality of mooring chain,” vol. 38, no. 2, pp. 112–117, 2009.
[7] R. R. Baracaldo, M. C. Santos, M. Arturo, and A. Echeverría, “Effect of flash butt welding parameters on mechanical properties of wheel rims,” vol. 23, no. 01, pp. 51–57, 2018.
[8] P. U. Nwachukwu and O. O. Oluwole, “Effects of rolling process parameters on the mechanical properties of hot-rolled St60Mn steel,” Case Stud. Constr. Mater., vol. 6, pp. 134–146, Jun. 2017.
[9] Y. Dong et al., “The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel,” Metals (Basel)., vol. 8, no. 10, p. 742, Sep. 2018.
[10] S. Ağca and G. Çankaya, “Multidisciplinary Studies and Innovative Technologies The Effect of Cold Rolling on Mechanical Properties of Zircaloy-4 †,” pp. 29–35, 2017.
Published
2019-09-12
Abstract viewed = 106 times
PDF (Bahasa Indonesia) downloaded = 85 times