KAJI EKSPERIMEN PERBAIKAN CACAT RONGGA BENDA CORAN MATERIAL FC 250 MELALUI PROSES PENGELASAN BERBASIS ELEKTRODA NIKEL
Abstract
Based on the case study in the field, it was found that the casting product had surface defects in the form of cavities and was then repaired using a nickel electrode-based welding method. This repair was carried out to close the cavity defects so that a perfect casting shape was obtained. The material that has been welded has a different hardness from the base material, making it difficult to machining. This study aims to analyze the effect of welding on the ability of gray cast iron material that has been welded in terms of cutting tool wear and chip formation. The sample used was made of gray cast iron with a weld bead on its surface. Welding used a CIN-1 nickel electrode with the SMAW (shielded metal arc welding) welding method. Cutting was carried out using a conventional milling process using an HSS dovetail cutter. Observations were made through hardness testing on the base material, PMZ (partially melted zone), and weld metal which was continued with microstructure testing, wear measurement and chips formed. Based on the results of observations of FC 250 material that was welded on the base material, the microstructure formed was pearlite with graphite in the form of thin and long flakes. The microstructure in PMZ is formed by martensite and carbide, while the microstructure in weld metal consists of an austenite matrix with even distribution of graphite particles. The microstructure formed affects the hardness value of the material. From the observation, the hardness between weld metal and base material is not much different, namely 219 HV and 224 HV. The hardness in PMZ is 385 HV.
Downloads
References
[2] T. Surdia and S. Saito, Pengetahuan Bahan Teknik, Keempat. Jakarta: PT Pradnya Paramita, 1999. [Online]. Available: http://etd.repository.ugm.ac.id/penelitian/detail/86075
[3] H. Wiryosumarto and T. Okumura, Teknologi Pengelasan Logam, vol. 8. 2000.
[4] D. Iman and H. Purwanto, “Pengaruh Pengelasan Besi Cor FC Dengan Metode Preheat dan Post Weld Heat Treatment Menggunakan Elektroda Paduan Nikel,” vol. 17, no. 1, pp. 13–17, 2021.
[5] M. S. Permana, R. Suratman, and B. Tarigan, “Bagaimana Memperbaiki Cacat Permukaan pada Komponen yang Terbuat dari Besi Cor,” Proceeding Semin. Nas. Tah. Tek. Mesin XI, no. SNTTM XI, pp. 1647–1656, 2012.
[6] ASTM A 159-83 (2001) Standar Spesification for Automotive Gray Iron Castings. 2001.
[7] D. L. Olson, T. A. Siewert, S. Liu, and G. R. Edwards, ASM Handbook Volume 6: Welding, Brazing, and Soldering, vol. 6. 1993.
[8] T. Rochim, Teori dan Teknologi Proses Pemesinan, 1st ed. Bandung: Institut Teknologi Bandung, 1993.
Copyright (c) 2024 Reza Yadi Hidayat, Antonius Adi Soetopo, Dede Buchori Muslim, Muhammad Nahrowi, Syifa Khairani
This work is licensed under a Creative Commons Attribution 4.0 International License.
The paper presented is assumed not to contain proprietary materials that are not protected by patents or patent applications. Responsibility for technical content and for protection from proprietary materials is the responsibility of the author and their organization and not the responsibility of the machine or its editorial staff. The primary author (first / appropriate) is responsible for ensuring that the article has been viewed and approved by all other authors. It is the responsibility of the author to obtain all copyright release permits required for the use of any copyrighted material in the manuscript before submission.