The Synthesis and Characterization Composite Fe3O4/Chitosan/Clay Bangka
synthesis and characterization composite Fe3O4/chitosan/clay Bangka
Abstract
Synthesis and characterization of Fe3O4/chitosan/clay Bangka has been carried out. Synthesis of composite was done with variations the composition of clay (0; 25; 50; 100 %) at the composition of Fe3O4 95 mg of Fe3O4 and 1 gr of chitosan. Characterization of composite Fe3O4/chitosan/clay have been analysed with XRD, FTIR, porosity test, the degree of development, and adsorption efficiency test for Cu2+ ion. The results of the analysed with XRD show the difractogram of clay and Fe3O4 at 2θ= 8,92o, 29,57o, and 45,61o (clay); 26,90o, and 35,64o (Fe3O4). Results of the analysed with ftir show the spectrum of the chitosan, clay, and Fe3O4 at 3825, 3689, 2103, 1425 cm-1 (chitosan), 1028, 884,41 cm-1 (clay), 791,11 cm-1 (chitosan) and 696,95 cm-1 (Fe3O4). The results of porosity test and the degree of development showed the high point are 1,547 and 754,63% without composition of clay. The adsorption test for Cu2+ ion show percentage of adsorption efficiency is 72,41% at composite of Fe3O4/chitosan with the clay added 1 gr.
Downloads
References
Anggasari, N., Alauhdin, M., dan Prasetya, A. T., 2013, Sintesis dan Karakterisasi Membran Kitosan-Tripolifosfat sebagai Alternatif Pengontrol Sistem Pelepasan Obat, Indo. J. Chem. Sci., 2(3):190-193.
Asriza, R.O., Fabiani, V.A. 2019. Remediasi Logam Seng (Zn) pada Air Bekas Tambang Timah Menggunakan Nanomagnetik Fe3O4/Kitosan Cangkang Rajungan (Portunus pelagicus). Indonesian Journal of Chemical Science 8 (3) (2019).
Badan Pusat Statistik, 2018, Ekspor Kepiting dan Kerang-kerangan Menurut Negara Tujuan Utama 2012-2015, (online) www.bps.go.id/linkTabelStatis/View/id/1020, diakses 10 desember 2019.
Cho, D.W., Jeon, B. H. dan Chon, C. M. (2012). A Novel Chitosan/Clay/Magnetite Composite For Adsorption of Cu (II) and As (V). Chem. Eng. J. 200, 654.
Dinas Kelautan dan Perikanan Provinsi Kepulauan Bangka Belitung. 2015. Statistik Perikanan Tangkap Provinsi Kepulauan Bangka Belitung. Bangka Belitung: Bidang Statistik DKP Provinsi Kepulauan Bangka Belitung.
Hastuti, Budi., Masykur, Abu., dan Ifada, Farida. 2011. Modifikasi Kitosan Melalui Proses Swelling Dan Krosslinking Menggunakan Glutaraldehid Sebagai Pengadsorpsi Logam Cr (VI) Pada Industri Batik. Jurnal EKOSAINS. Vol. III. No. 3.
Hong, S., Chang, Y., and Rhee, I. 2020. Chitosan-Coated Ferrite (Fe3O4) Nano particles As A T2 Contrast Agent For Magnetic Resonance Imaging. Journal Of The Korean Physical Society, 56 (3): 868-873.
Indrawati, D. dan S. E. Cahyaningrum. 2013. Pengaruh Perbandingan Komposisi Kitosan dan Silika Terhadap Karakterisasi Adsorben Kitosan-Silika Bead. UNESA Journal of Chemistry, 2 (1): 8-13.
Junisu, B.A., Handayani, E., Ismuyanto, B., Saptati, A.S., Hidayati, N. dan Himma, N.F. 2017. Pengaruh Penambahan Kitosan Terhadap Efektivitas Proses Koagulasi Menggunakan Besi (III) Klorida Heksahidrat. Jurnal Rekayasa Bahan Alam dan Energi Berkelanjutan, Vol. 1, No. 2, 2017, PP 63-69.
Kusumaningsih, T., Handayani, D.S., dan Lestari, Y. (2012). Pembuatan Mikrokapsul Kitosan Gel Tersambung
Silang Etilen Glikol Diglisidil Eter Sebagai Adsorben Warna Procion Red Mx8b. AL-CHEMY Jurnal Penelitian Kimia. 8(1) : 47-56.
Le, V.T., Tran, B.C., Tran, T.K.N., Tran, X.V., Nguyen, D.D., Nguyen, M.H., Dang, T.T.T., Nguyen, T.H., and Le, H.S., 2017. Preparation Of Cross-linked Magnetic Chitosan Particles From Steel Slag And Shrimp Shells For Removal Of Heavy Metals. Environmental Technology Journal.http://dx.doi.org/10.1080/09593330.2017.1337236.
Ma W., Dai J., Dai X., & Yan Y. 2014. Preparation and Characterization of Chitosan/Clay/ Fe3O4 Magnetic Microspheres and Their Application for The Removal of Ciprofloxacin. Journal of Adsorption Science & Technology. Vol. 32, No. 10, 2014, 776-777.
Maylani, A. S., Sulistyaningsih, T., dan Kusumastuti, E. 2016. Preparasi Nanopartikel Fe3O4 (Magnetit) Serta Aplikasinya Sebagai Adsorben Ion Logam Kadmium. Indonesian Journal of Chemical Science. 5 (2) (2016).
Noralia, E. dan D.K. Maharani. 2013. Filtrasi Ion Logam Cr6+ Dengan Membran Komposit Kitosan Silika. UNESA Journal of Chemistry, 2 (1): 24-28.
Novi, Y., Zaharah, T.A., dan Destiarti, L. 2016. Sintesis dan Karakterisasi Membran Komposit Kitosan-Kaolin. Jurnal Kimia Khatulistiwa. Vol. 5 (4), 47-56. ISSN. 2303-1077.
Rahmayani, N. 2017. Sintesis Dan Pencirian Partikel Magnetik Fe Hasil Reduksi Natrium Borohidrida Dalam Hidrogel Kitosan. Skripsi FMIPA Kimia. Institut Pertanian Bogor.
Sadiana, I.M., Fatah, A.H., dan Karelius. 2017. Sintesis Komposit Lempung Alam Magnetit Sebagai Adsorben Zat Warna Methylene Blue. Jurnal Sains dan Terapan Kimia. Vol. 11, No. 2, 90-102.
Saiful, Nurfitriana, Ramli, M., Maulana, I. 2013. Pengembangan Membran Magnesol Untuk Pemurnian Biodiesel. Jurnal Rekayasa Kimia Dan Lingkungan, Vol. 9, No. 3, Hlm. 118-125.
Setyaningrum, D. 2014. Sintesis Membran Kitosan-Silika Abu Sekam Padi Untuk Filtrasi Ion Cd2+ dan Cu2+, Skripsi. Universitas Negeri Semarang.
Silverstein, R. M., F.X. Webster, and D. Kiemle, Spectrometric Identification of organic compounds, 7 th ed., John Wiley, New York, 2005.
Susilowati, S., Triyono, Nawangsi, E., dan Widiyati, S. (2013). Pengaruh Zat Aditif THFA Terhadap Porositas Dan Luas Muka Kernel U3O8 Hasil Gelasi Eksternal. Yogyakarta: Batan.
Tanasale, M.F., Killay, A.., Laratmase, M.S. (2012). Kitosan Dari Limbah Kulit Kepiting Rajungan (Portunus sanginolentus L.) Sebagai Adsorben Zat Warna Biru Metilena. Jurnal Natur Indonesia, 14 (2), 165-171.
Tanheitafino, S., Zaharah, T. A., dan Destiarti, L., 2016, Modifikasi Kitosan dengan Kaolin dan Aplikasinya sebagai Adsorben Timbal (II), J. Kimia Khatulistiwa, 5 (2), 33-42.
Yulianis, Mahidin, dan Muhammad, S. 2017. Adsorpsi Ion Logam Tembaga Menggunakan Nano Zeolit Alam Yang Diaktivasi. Jurnal Litbang Industri Vol. 7, No. 1, 61-69.
Zahara, T. A., Shofiyani, A., dan Sayekti, E., 2015, Karakteristik Biomassa Chlorella sp Terimobilisasi pada Kitosan untuk Adsorpsi Kromium (III) dalam Larutan, Alchemy, Vol. 11 (1); 15-28.