PENGARUH PARAMETER PENGELASAN RESISTANCE SPOT WELDING TERHADAP SIFAT FISIK DAN MEKANIK MULTI-LAYER lOGAM TAK SEJENIS BERBEDA KETEBALAN
RESISTANCE SPOT WELDING
Joining three sheets by resistance spot welding was an increasing trend in automotive assembly. Effect parameter of welding such us voltage and welding times to physics and mechanical properties resistance spot weld joint dissimilar metals three sheets 316L, SS 400, J1 was determined. Electroda pressure was kept constant in this result. The parameter of welding was used in this experiment were 2.02; 2.30; 2.67 V and 3; 4; 5; 7.5 s. As a result of the experiment, it was determined that voltage 2.67 V and welding times 7.5 s result tensile shear load was 11.19 kN with pull out failure mode. The increasing of voltage and welding times cause higher fusion zone size along sheet/sheet interface. The area of HAZ was increased because there was an increase in the welding times. The higher hardness was a nugget because grain was formed columnar.
 M. Vural, A. Akkuş, and B. Eryürek, "Effect of welding nugget diameter on the fatigue strength of the resistance spot welded joints of different steel sheets," Journal of Materials Processing Technology, vol. 176, pp. 127-132, 2006.
 H. Eizadi and S. Marashi, "On the resistance spot welding of four-sheet stack of unequal sheet thickness," Science and Technology of Welding and Joining, vol. 21, pp. 632-637, 2016.
 Y. Li, F. Yan, Z. Luo, Y. Chao, S. Ao, and X. Cui, "Weld growth mechanisms and failure behavior of three-sheet resistance spot welds made of 5052 aluminum alloy," Journal of Materials Engineering and Performance, vol. 24, pp. 2546-2555, 2015.
 S. Wei, R. Liu, D. Lv, L. Lin, R. Xu, J. Guo, et al., "Weldability and mechanical properties of similar and dissimilar resistance spot welds of three-layer advanced high strength steels," Science and Technology of Welding and Joining, vol. 20, pp. 20-26, 2015.
 R. Chtourou, N. Leconte, F. Chaari, G. Haugou, É. Markiewicz, and B. Zouari, "Macro-modeling of the strength and failure of multi-layer multi-steel grade spot welds: Connector formulation, assembly model and identification procedure," Thin-Walled Structures, vol. 113, pp. 228-239, 2017.
 C. V. Nielsen, K. S. Friis, W. Zhang, and N. Bay, "Three-sheet spot welding of advanced high-strength steels," Welding journal, vol. 90, 2011.
 N. Ma and H. Murakawa, "Numerical and experimental study on nugget formation in resistance spot welding for high strength steel sheets in automobile bodies," Transactions of JWRI, vol. 38, pp. 19-24, 2009.
 M. Pouranvari and S. Marashi, "Critical sheet thickness for weld nugget growth during resistance spot welding of three‐steel sheets," Science and Technology of Welding and Joining, vol. 16, pp. 162-165, 2011.
 S. Aslanlar, "The effect of nucleus size on mechanical properties in electrical resistance spot welding of sheets used in automotive industry," Materials & Design, vol. 27, pp. 125-131, 2006.
 F. Hayat, "Resistance spot weldability of dissimilar materials: BH180-AISI304L steels and BH180-IF7123 steels," Journal of Materials Science & Technology, vol. 27, pp. 1047-1058, 2011.
 W. Harsono and T. Okumura, "Teknologi Pengelasan Logam Pradnya Paramita," ed: Jakarta, 1981.
Copyright (c) 2021 Haikal Haikal
This work is licensed under a Creative Commons Attribution 4.0 International License.
The paper presented is assumed not to contain proprietary materials that are not protected by patents or patent applications. Responsibility for technical content and for protection from proprietary materials is the responsibility of the author and their organization and not the responsibility of the machine or its editorial staff. The primary author (first / appropriate) is responsible for ensuring that the article has been viewed and approved by all other authors. It is the responsibility of the author to obtain all copyright release permits required for the use of any copyrighted material in the manuscript before submission.